OK AristoRod™ 55是一种适合高强度钢GMAW焊接的0.5Cr-0.5Ni-0.2Mo合金化实芯焊丝。OK AristoRod™ 55经过伊萨独有的先进表面特性(ASC)技术处理，其可将MAG焊接操作提升到全新高度，并且在机器人和自动化焊接中具有全方位的高效性。其特性包括优良的引弧性能；无故障高速送丝和远距离送丝；较高焊接电流下电弧极其稳定；飞溅少；较低烟尘排放；导电嘴磨损少且焊丝腐蚀防护得到改善。

Typical Tensile Properties

As welded
保护气体	Elongation	Tensile Strength	Yield Strength	Stress Relieved Temperature	Stress Relieved Testing Time
AWS 80Ar/20CO2(M21)	-	-	-	-	-
EN 80Ar/20CO2(M21)	20 %	770 MPa	690 MPa	-	-
Stress relieved
保护气体	Elongation	Tensile Strength	Yield Strength	Stress Relieved Temperature	Stress Relieved Testing Time
EN 80Ar/20CO2(M21)	24 %	750 MPa	660 MPa	620 °C	1 hr
EN 80Ar/20CO2(M21)	24 %	750 MPa	660 MPa	570 °C	1 hr

 

夏比V型缺口冲击性能

As welded
Impact Value	Testing Temperature	保护气体	Stress Relieved Testing Temp	Stress Relieved Testing Time
80 J	0 °C	EN 80Ar/20CO2(M21)	-	-
75 J	-20 °C	EN 80Ar/20CO2(M21)	-	-
65 J	-30 °C	EN 80Ar/20CO2(M21)	-	-
60 J	-40 °C	EN 80Ar/20CO2(M21)	-	-
50 J	-50 °C	EN 80Ar/20CO2(M21)	-	-
50 J	-60 °C	EN 80Ar/20CO2(M21)	-	-
Stress relieved
Impact Value	Testing Temperature	保护气体	Stress Relieved Testing Temp	Stress Relieved Testing Time
95 J	0 °C	EN 80Ar/20CO2(M21)	620 °C	1 hr
70 J	-20 °C	EN 80Ar/20CO2(M21)	620 °C	1 hr
55 J	-30 °C	EN 80Ar/20CO2(M21)	620 °C	1 hr
40 J	-50 °C	EN 80Ar/20CO2(M21)	620 °C	1 hr
60 J	-20 °C	EN 80Ar/20CO2(M21)	570 °C	1 hr
50 J	-40 °C	EN 80Ar/20CO2(M21)	570 °C	1 hr
35 J	-60 °C	EN 80Ar/20CO2(M21)	570 °C	1 hr

 

焊缝金属分析

Mn
Mn	Mo	C	Si	Ni	Cr
1.38 %	-	-	-	-	-
Mo
Mn	Mo	C	Si	Ni	Cr
-	0.20 %	-	-	-	-
C
Mn	Mo	C	Si	Ni	Cr
-	-	0.12 %	-	-	-
Si
Mn	Mo	C	Si	Ni	Cr
-	-	-	0.71 %	-	-
Ni
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	0.53 %	-
Cr
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	-	0.58 %

 

熔敷数据

安培	熔敷率	电压 V	直径	送丝速度
40-170 A	0,4-2,6 kg/h	16-22 V	0.8 mm	2-10,8 m/min
80-280 A	1-5,4 kg/h	18-28 V	1.0 mm	2,7-14,7 m/min
120-350 A	1,5-6,6 kg/h	20-33 V	1.2 mm	2,7-12,4 m/min
225-480 A	3,3-11,6 kg/h	26-38 V	1.6 mm	3,5-12,0 m/min