OK AristoRod™ 69是一种适合要求具有低温冲击韧性高强度钢GMAW焊接的0.3Cr-1.4Ni-0.25Mo合金化实芯焊丝。OK AristoRod™ 13.29经过伊萨独有的先进表面特性(ASC)技术处理，其可将MAG焊接操作提升到全新高度，并且在机器人和自动化焊接中具有全方位的高效性。其特性包括优良的引弧性能；无故障高速送丝和远距离送丝；较高焊接电流下电弧极其稳定；飞溅少；较低烟尘排放；导电嘴磨损少且焊丝腐蚀防护得到改善。

Typical Tensile Properties

As welded
Elongation	Tensile Strength	Yield Strength	保护气体	Stress Relieved Temperature	Stress Relieved Testing Time
17 %	805 MPa	715 MPa	AWS 80Ar/20CO2(M21)	-	-
19 %	800 MPa	730 MPa	EN 80Ar/20CO2(M21)	-	-
Stress relieved
Elongation	Tensile Strength	Yield Strength	保护气体	Stress Relieved Temperature	Stress Relieved Testing Time
20 %	750 MPa	690 MPa	EN 80Ar/20CO2(M21)	620 °C	15 hr

 

夏比V型缺口冲击性能

As welded
Impact Value	Testing Temperature	保护气体	Stress Relieved Testing Temp	Stress Relieved Testing Time
100 J	20 °C	EN 80Ar/20CO2(M21)	-	-
73 J	-40 °C	EN 80Ar/20CO2(M21)	-	-
Stress relieved
Impact Value	Testing Temperature	保护气体	Stress Relieved Testing Temp	Stress Relieved Testing Time
130 J	20 °C	EN 80Ar/20CO2(M21)	620 °C	15 hr
60 J	-20 °C	EN 80Ar/20CO2(M21)	620 °C	15 hr
60 J	-30 °C	EN 80Ar/20CO2(M21)	620 °C	15 hr

 

焊缝金属分析

Mn
Mn	Mo	C	Si	Ni	Cr
1.54 %	-	-	-	-	-
Mo
Mn	Mo	C	Si	Ni	Cr
-	0.24 %	-	-	-	-
C
Mn	Mo	C	Si	Ni	Cr
-	-	0.089 %	-	-	-
Si
Mn	Mo	C	Si	Ni	Cr
-	-	-	0.53 %	-	-
Ni
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	1.23 %	-
Cr
Mn	Mo	C	Si	Ni	Cr
-	-	-	-	-	0.26 %

 

熔敷数据

安培	熔敷率	电压 V	直径	送丝速度
80-280 A	1-5,4 kg/h	18-28 V	0.8 mm	2,7-14,7 m/min
80-280 A	1-5,4 kg/h	18-28 V	0.9 mm	2,7-14,7 m/min
80-280 A	1-5,4 kg/h	18-28 V	1.0 mm	2,7-14,7 m/min
120-350 A	1,5-6,6 kg/h	20-33 V	1.2 mm	2,7-12,4 m/min
225-480 A	3,3-0 kg/h	26-38 V	1.6 mm	3,1-8,1 m/min